C |
S |
P |
Si |
Mbak |
Ti |
Co |
Cr |
Fe |
Zr |
Cu |
B |
Al |
≤ |
||||||||||||
0,13 |
0,015 |
0,02 |
0,8 |
0,4 |
2.0-3.0 |
15.0-21.0 |
18.0-21.0 |
≤1.5 |
≤0.15 |
≤0.2 |
0.02 |
1.0-2.0 |
Kapadhetan (g / cm3) |
Titik lebur (℃) |
Konduktivitas termal (W / m · ℃) |
Modulus elastis MPa) |
Koefisien ekspansi termal 10-6℃-1) |
8.2 | 1400 | 21.76 (100 ℃) | 225 | 12.71 (20-100 ℃) |
Perawatan panas | Kekuwatan sing kuat (MPa) |
Ngasilake kekuwatan (MPa) |
Elongasi (%) |
Perawatan solusi | 820 | 590 | 8 |
Bar / Rod | Kabel | Strip / Koil | Lembar / Plate | Pipa / Tabung |
BS HR2, HR501, HR502 lan HR503; SAE AMS 5829; AECMA PrEN 2295, 2296
2297, 2400, 2401, 2669 lan 2670.
|
BS HR202, AECMA PrEN 2298
|
BS HR402, AECMA PrEn 2299
|
Paduan iki utamane nguatake tahap 3'i3 (Ti 、). Deformasi sepuh saka superalloy basa nikel kobalt, ngemot kobalt sing akeh lan
macem-macem unsur penguat, kekuwatan tarik sing luwih dhuwur lan resistensi creep ing 815 ~ 870 ℃, resistensi oksidasi lan korosi sing apik, resistensi sing apik
ing kadhemen lan panas maneh lan maneh kanthi tumindak gantian, nuduhake kekuatan lemes sing dhuwur lan formabilitas sing apik lan stabil
• Disk turbin Mesin Turbin • Blade • Sealing ring lan elemen elastis
• pengikat suhu tinggi • Dering ealing clamp lan elemen elastis, lsp